在光通信关键技术中使用我们提供的粘合剂技术。
特点
折射率可以被精确地控制在1.46-1.57±0.005 Na-D.的范围内。
使用紫外线固化很容易对准。高温、高湿环境下附着力仍然表现优异，提供高可靠的耐久性。
产品选型
Model
[Main
ingredient] Curing
conditions [irradiation
level &
time] Refraction
index *1 Viscosity
cP Glass
transition
temperature
Tg °C Optical
transmittance%
[1.3um] Bond
Strength
kgf/cm2 Special
Features
Refractive
Index
Adjusting
Material
High Tg
[Epoxy]*2 30mW/cm2
10min 1.46~1.57 200~560 130~137 89~90 120~180 Modulate the refractive index to specific values for the best level of transparency.
Refractive
Index
Adjusting
Material
Low Tg
[Epoxy] 10mW/cm2
10min 1.45~1.57 200~560 49~67 86~90 180 Modulate the refractive index to specific values for the best level of transparency
GA700H
High Tg
[Epoxy]*2 30mW/cm2
10min 1.46 252 138 93 94 At λ1.55um, adjusted to match silica glass
GA700L
Low Tg
[Epoxy] 10mW/cm2
5min 1.46 250 49 94 200 At λ1.55um, adjusted to match silica glass
AT6001
[Acrylate] 10mW/cm2
10min 1.51 440 -3 91 150 Telecordia standard strong under high temperature and humidity, flexible
AT8224
[Acrylate] 10mW/cm2
5min 1.51 180 111 89 122 Telecordia standard strong under high temperature and humidity, High Tg
AT6390
[Acrylate] 10mW/cm2
5min 1.51 840 100 90 156 High endurance material,
Tg 100°C,
High viscosity
*1 : Na-D line after hardening.
*2 : Content product is "Non-medical use, rious substance" Please refer to SDS for handling.
&169 2000 NTT Advanced Technology Corporation