多边化裂纹焊接时，裂纹多发生在受高温的金属中，其部位并不都紧靠熔合线。这说明裂纹的产生和晶界液化并无关系。焊缝或进焊缝区在固相线以下的高温区域，由于刚凝固的金属存在很多晶格缺陷和 严重的物理及化学部均匀性，在一定的温度和应力作用下，由于晶格缺陷的移动和聚集，便形成了二次边界， 即所谓的多边化边界，这个边界上堆积了大量的晶格缺陷，所以它的组织疏松，高温时的强度和塑性都降低， 只要在此时受到少量的拉伸变形，就会沿多变化的边界裂开即为多边化裂纹。
In the process of polygonal crack welding, cracks occur mostly in high temperature metals, and their locations do not all depend on fusion lines. This indicates that there is no relationship between crack generation and grain boundary liquefaction. The two boundary, the so-called multilateralism boundary, is formed by the movement and aggregation of lattice defects due to the movement and accumulation of lattice defects under certain temperature and stress, because of the existence of many lattice defects and the serious uniformity of the physical and chemical parts of the rigid solidified metal. A large number of lattice defects are accumulated, so its tissue is loose and the strength and plasticity at high temperature are reduced. As long as a small amount of tensile deformation occurs at this time, a multilateral crack will be cracked along the multivariable boundary.
冷裂纹的特征:从冷裂纹的产生条件及形成原因看，它与其它焊接裂纹有着本质的区别。这些区别构成了冷 裂纹的主要的特征。这些特征可作为判别裂纹性质的主要依据。冷裂纹的特征主要表现在以下几个方面,冷裂纹的形成温度大量研究结果表明，对钢材来说冷裂纹形成的温度大体在100~-100°C之间，具体温 度随母材与焊接条件不同而异.
The characteristics of cold cracks: from the generation conditions and causes of cold cracks, they are essentially different from other welding cracks. These differences constitute the main characteristics of cold cracks. These characteristics can be used as the main basis for judging the nature of cracks. The characteristics of cold crack are mainly shown in the following aspects. A large number of research results of cold crack formation temperature show that the temperature of cold crack formation for steel is approximately 100~-100 C, and the specific temperature varies with the parent material and the welding condition.
&8203 泰安扬帆数控科技有限公司咨询电话 0538－座落在风景秀丽的泰山脚下，东平湖畔，东临泰 山，西依黄河，南与孔孟故里相望。京沪高铁、济广高速公路贯穿而过，交通非常便利。
泰安扬帆数控科技有限公司目前是该地区一家从事焊接自动化装备的高新技术企业。集设计研发、 制 造和销售为一体，目前公司下设生产部、技术部、质检部、电控部、行政部、售后服务部、销售部等多个部 门 。
泰安扬帆数控科技有限公司（）主要产品有焊接自动化成套装备、数控切割机、工业焊接机器 人 和数字化逆变焊接电源、焊缝跟踪系统及焊接摆动器等，是一家综合技术实力的自动化、智能化焊接成 套 装备的供应商。产品广泛应用于国内外机械制造、化工、汽车配件制造、农用机械、建筑、金属波纹管、太 阳 能热水器、电热水器、不锈钢制品等多个领域，在各个地区，产量和性能都受到了用户的一致好评 。
泰安扬帆数控科技有限公司将秉承“以质量求生存，以管理求效益，以科技求发展”的文化理念，继往开 来 ，努力拼搏，奋发向上，创造民族自动化焊接！
泰安扬帆数控科技有限公司
地址：山东省泰安市东平县东平工业园区
电话：
销售热线：
传真：
QQ号：
联系人：卜经理
公司网址: http://www.tayfsk.com/
免费发布信息：http://www.lushangyun.com/
济南微信推广www.weidaoshang.com/
诺商商道系统，-互联网应用服务提供商：www.chinanovo.net/
诺商商道系统，-互联网应用服务提供商：www.cn-un.net/
诺商基于多年的优化经验和基础推出的诺商商道系统，诺商信息您身边的互联网！