液化裂纹的敏感温度区间是在固相线以下稍低的温度，及从低熔的晶间第二相开始熔化的温度到它全部熔 化的且部分晶间金属也开始熔化的温度。在焊缝金属中，多边化裂纹虽然是沿晶界发生和发展，但它是沿着新生的二次晶界分布的，裂纹附近常伴有再结晶晶粒的出现。或沿迁移后 的晶界，或沿再结晶晶界，而不是沿一次晶界分布。因此，裂纹的发展方向与一次结晶晶界毫无关系。这是多 边化裂纹的重要标志。
The sensitive temperature range of the liquefied crack is a slightly lower temperature below the solid phase line, and the melting temperature from the second phase of the low melting intercrystal to the melting temperature of it and the melting of some intercrystalline metals. In the weld metal, although the multilateralism crack occurs and develops along the grain boundary, it is distributed along the new two grain boundaries, and the cracks often occur with recrystallized grains near the crack. Or along the migrated grain boundaries, or along recrystallized grain boundaries, rather than along the grain boundaries. Therefore, the development direction of crack has nothing to do with the crystalline grain boundary. This is an important sign of the multilateralism crack.
多边化裂纹焊接时，裂纹多发生在受高温的金属中，其部位并不都紧靠熔合线。这说明裂纹的产生和晶界液化并无关系。焊缝或进焊缝区在固相线以下的高温区域，由于刚凝固的金属存在很多晶格缺陷和 严重的物理及化学部均匀性，在一定的温度和应力作用下，由于晶格缺陷的移动和聚集，便形成了二次边界， 即所谓的多边化边界，这个边界上堆积了大量的晶格缺陷，所以它的组织疏松，高温时的强度和塑性都降低， 只要在此时受到少量的拉伸变形，就会沿多变化的边界裂开即为多边化裂纹。
In the process of polygonal crack welding, cracks occur mostly in high temperature metals, and their locations do not all depend on fusion lines. This indicates that there is no relationship between crack generation and grain boundary liquefaction. The two boundary, the so-called multilateralism boundary, is formed by the movement and aggregation of lattice defects due to the movement and accumulation of lattice defects under certain temperature and stress, because of the existence of many lattice defects and the serious uniformity of the physical and chemical parts of the rigid solidified metal. A large number of lattice defects are accumulated, so its tissue is loose and the strength and plasticity at high temperature are reduced. As long as a small amount of tensile deformation occurs at this time, a multilateral crack will be cracked along the multivariable boundary.
泰安扬帆数控科技有限公司咨询电话 0538－座落在风景秀丽的泰山脚下，东平湖畔，东临泰 山，西依黄河，南与孔孟故里相望。京沪高铁、济广高速公路贯穿而过，交通非常便利。
泰安扬帆数控科技有限公司目前是该地区一家从事焊接自动化装备的高新技术企业。集设计研发、 制 造和销售为一体，目前公司下设生产部、技术部、质检部、电控部、行政部、售后服务部、销售部等多个部 门 。
泰安扬帆数控科技有限公司（）主要产品有焊接自动化成套装备、数控切割机、工业焊接机器 人 和数字化逆变焊接电源、焊缝跟踪系统及焊接摆动器等，是一家综合技术实力的自动化、智能化焊接成 套 装备的供应商。产品广泛应用于国内外机械制造、化工、汽车配件制造、农用机械、建筑、金属波纹管、太 阳 能热水器、电热水器、不锈钢制品等多个领域，在各个地区，产量和性能都受到了用户的一致好评 。
泰安扬帆数控科技有限公司将秉承“以质量求生存，以管理求效益，以科技求发展”的文化理念，继往开 来 ，努力拼搏，奋发向上，创造民族自动化焊接！
泰安扬帆数控科技有限公司
地址：山东省泰安市东平县东平工业园区
电话：
销售热线：
传真：
QQ号：
联系人：卜经理
公司网址: http://www.tayfsk.com/
免费发布信息：http://www.lushangyun.com/
济南微信推广www.weidaoshang.com/
诺商商道系统，-互联网应用服务提供商：www.chinanovo.net/
诺商商道系统，-互联网应用服务提供商：www.cn-un.net/
诺商基于多年的优化经验和基础推出的诺商商道系统，诺商信息您身边的互联网！