MATERIAL SPECIFIC RESISTANCE (Ω–CM/F) MELTING POINT °C COMPOSITION
Aluminum
1 ALUMINUM 1% SILICON 15.2 657
2 ALUMINUM 1199 15.97 660 Al99.99%
3 ALUMINUM EC 1350 16.83 657 Al99.45%
4 ALUMINUM 2024 20.25 638 Al93.84%Cu4.5%Mg1.5%Mn0.16%
5 ALUMINUM 3003 20.25 634 Al98.8%Mn1.2%
6 ALUMINUM 4043 25 632 Al94.75%Si5.25%
7 ALUMINUM 5005 19.95 652 Al99.2%Mn0.8%
8 ALUMINUM 5052 10.23 649 Al97.25%Cr0.25%Mn2.5%
9 ALUMINUM 5056 35.79 638 Al94.6%Cr0.1%Mg0.1%Mn0.1%
10 ALUMINUM 6061 23.04 649 Al97.9%Cr0.25%Cu0.25%Mg1%Si0.6%
Copper
1 ALLOY 725 94.3 1060 Cu88.2%Ni9.5%Sn2.3%
2 BE COPPER ALLOY 10 CDA 175 22.8 1029 Be0.55%Co2.55%Cu96.9%
3 BE COPPER ALLOY 25 CDA 172 46.2 865 Be1.8%Cu98.1%
4 BE COPPER CDA 17410 36.9 1025 Be0.3%Co0.5%Cu99%
5 BRASS FREE-CUT CDA 360 39.9 885 Cu61.5%Pb3.1%Zn35.4%
6 BRASS 7030 CDA 230 37 915 Cu70%Zn30%
7 BRASS GILDING CDA 210 18.5 1050 Cu95%Zn5%
8 CADMIUM COPPER CDA 162 11.5 1030 Cd1%Cu99%
9 COMMERCIAL BRONZE 90% CDA 220 23.6 Cu90%Zn10%
10 COPPER 27% NICKEL CLAD 14 1100 Cu99.9%Ni99%
11 COPPER 99.95% CDA 102 OF 10.3 1083 Cu99.5%min
12 COPPER 99.99% CDA 101 10.3 1083 Cu99.99%min
13 COPPER ETP MAGNET WIRE 10.3 Cu99.9%min
14 COPPER NICKEL 20% 160 1150 Cu79%Ni21%
15 COPPER ZIRCONIUM CDA 150 11.2 980 Cu99.85%Zr0.15%
16 CUPRO NICKEL 70-30 225 1170 Cu69.5%Fe0.5%Ni30%
17 LOW BRASS CDA 240 32.4 965 Cu80%Zn20%
18 NICKEL SILVER CDA 752 173 1070 Cu65%Ni18%Zn17%
19 NICKEL SILVER CDA 757 130 1040 Cu65%Ni12%Zn23%
20 NICKEL SILVER CDA 764 189 1020 Cu60%Ni18%Zn22%
21 PD-135 11.3 1080 Cd1%maxCr1%maxCu99%min
22 PH BRONZE 5% CDA 510 A 69.1 950 Cu94.8%P0.2%Sn5%
23 PH BRONZE 8% CDA 521 C 79.8 880 Cu92%P0.16%Sn8%
24 PH BRONZE 10% CDA 524 D 94.3 845 Cu90%Sn10%
Nickel
1 ALLOY 99 48 1450 Ni99.8%min
2 DURANICKEL 301 255 1450 Al4%-4.75%Ni93%Ti0.25%-1%
3 MONEL 400 290 1350 Cu32.5%Fe2.5%Mn2%Ni63%
4 MONEL 404 319 1299 Cu43%-48%Ni52%-57%
5 Monel K 500 370 Al2.3%-3.15%Cu23.35%-34.5%Fe2%maxMn1.5%maxNi63%-70%
6 NICKEL 205 50 1450 Ni99.45%min
7 NICKEL 211 102 1430 Mn4.75%Ni93.7%
8 NICKEL 220 45 1450
9 NICKEL 270 45 1450 Ni99.97%min
10 NICKEL A/200 48 1450 Ni99%min
Precious Metal
1 ALLOY 20-245 245
2 ALLOY 406 75
3 ALLOY 411 37.0009 Ag89%Pd11%
4 ALLOY 417 57
5 ALLOY 422 180 1880
6 ALLOY 443 80
7 ALLOY 446 190
8 ALLOY 486 610 1700
9 GOLD 99.99% BE MOD 12.6 1063 Au99.99%min
10 GOLD 99.99% 14.14 1063 Au99.99%min
11 PALLADIUM 60 1554 Pd99%min
12 PLATINUM 8% TUNGSTEN 400 1870 Pt92%W8%
13 PLATINUM 10% IRIDIUM 150 1775 Ir10%Pt90%
14 PLATINUM 10% RHODIUM 111 1850 Pt90%Rh10%
15 PLATINUM 20% IRIDIUM 186 1840 Ir20%Pt80%
16 PLATINUM 20% RHODIUM 125 1900 Pt80%Rh20%
17 PLATINUM PURE TC GRADE 64 1773 Pt99.99%min
18 RHODIUM 99.8% 30 1960 Rh99.8%min
19 SILVER 99.99% 8.8 960 Ag99.99%
Resistance Wire
1 MANGANIN 230 SHUNT 230 1020 Cu84%Mn12%Ni4%
2 MANGANIN 290 290 1020 Cu84%Mn12%Ni4%
3 NICKEL ALLOY 30 30 1100 Cu98%Ni4%
4 NICKEL ALLOY 60 60 1100 Cu94%Ni6%
5 NICKEL ALLOY 90 90 1100 Cu90%Ni10%
6 NICKEL ALLOY 120 120 1425 Fe30%Ni70%
7 NICKEL ALLOY 180 180 1100 Cu78%Ni22%
8 NICO 294 1210 Cu55%Ni45%
9 NIFE 5200 120 1425 Fe30%Ni70%
10 STABLOHM 610 (TOPHET D) 610 1300 Cr20%Fe45%Ni35%
11 STABLOHM 650 650 1395 Cr20%Ni80%Si1%-2%
12 STABLOHM 675 675 1350 Cr16%Fe34%Ni60%
13 STABLOHM 710 710 1377 Cr30%Ni70%
14 STABLOHM 750 750 1510 Al4%Cr15%Fe81%
15 STABLOHM 800 A 800 1395 Al2.5%Cr20%Cu2.5%Ni75%
16 STABLOHM 812 812 1510 Al4.5%Cr21%Fe74.5%
17 STABLOHM 875 875 1520 Al5.5%Cr22.5%Fe72%
Stainless Steel
1 STAINLESS STEEL 302 420 1399
2 STAINLESS STEEL 304 420 1399
3 STAINLESS STEEL 305 420 1399
4 STAINLESS STEEL 308 455 1399
5 STAINLESS STEEL 309 170 1399
6 STAINLESS STEEL 310 520 1399
7 STAINLESS STEEL 316 470 1371
8 STAINLESS STEEL 316L 445 1399
9 STAINLESS STEEL 347 470 1399
10 STAINLESS STEEL 4