电极红铜分类
紫铜类（纯铜）：T2.C1100.C11000.无氧铜TU1.C1020.C10200加磷脱氧铜TP2.C1220.C12200.
黄铜类，铜合金
H96.C2100.C21000.H90.C2200.C22000.H85.C2300.C23000.H80.C2400.C24000.H68A.C2680. C26200.H65.C2700.C26800.H62
压铸模具配件批发
电极红铜分类
紫铜类（纯铜）：T2.C1100.C11000.无氧铜TU1.C1020.C10200加磷脱氧铜TP2.C1220.C12200.
黄铜类，铜合金
H96.C2100.C21000.H90.C2200.C22000.H85.C2300.C23000.H80.C2400.C24000.H68A.C2680. C26200.H65.C2700.C26800.H62.C2720.C27400.
铅黄铜 HPb59-1.C3710.C37800.HPb59-2.C3771.C35300. HPb60-2.C3604.C36000.HPb63-3.C3560.C34500.HPb63-0.1.C34900.
铝黄铜HAi77-2.C6870.C68700. HAi60-1-1.C6782.C67000.HAi59-3-2.C67800.HAi66-6-3-2.C6872.
锡黄铜HSn62-1.HSn70-1AB.锰黄铜HMn58-2.C67400.HMn57-3-1.铁黄铜HFe59-1-1.C6782.C67820.硅黄铜HSi80-3.C69400.
青铜类：
锡青铜QSn4-3,QSn6.5-0.1.QSn7-0.2.C5212.C52100.QSn6.5-0.4.
铝青铜QAi9-2.C61000.QAi9-4.QAi10-3-1.5. C6161.C61900.QAi10--4-4.C6301.C63000.C63200.
硅青铜QSi3-1.C65500.C65800.QSi1-3.C64700.QSi1.8. 锰青铜QMn5.锆青铜QZr0.2-0.4.铬青铜QCr0.5.C18100.C18200.C18400.QCr1-2.
铬锆铜QCr1-0.15.C18150. 镉青铜QCd1.0.铍青铜QBe1.8.QBe2.0.白铜类：B19.B25.铁白铜BFe10-1--1.B111.C70600.BFe30--1-1.B111. C71500.
锌白铜BZn15-20.等。
电极红铜
紫铜是比较纯净的一种铜，一般可近似认为是纯铜，导电性、塑性都较好，但强度、硬度较差一些。紫铜具有优良的导热性﹑延展性和耐蚀性。紫铜中的微量杂质对铜的导电、导热性能有严重影响。其中钛、磷、铁、硅等显著降低电导率,而镉、锌等则影响很小。电极红铜铜合金（copperalloy）以纯铜为基体加入一种或几种其他元素所构成的合金。氧、硫、硒、碲等在铜中的固溶度很小,可与铜生成脆性化合物,对导电性影响不大，但能降低加工塑性。
镍：NiNi能提高钢的淬透性；Ni能细化晶粒
硫（S）常以MnS形式存在钢中，割裂基体的连续性，恶化材料的韧性、抗腐蚀性、抛旋光性、放电加工性、蚀纹性，可提高材料的切削能力。
2. 冶炼工艺普通炼钢工艺
电渣重熔（ESR）将粗钢坯置于电渣炉中，通入强电流，使电炉产生很高的温度，使粗钢坯熔化成钢水，钢水流经电渣，杂质被电渣过滤吸附，从而达到纯化的效果。整体重熔速度快，但一些非常细小的杂质并未除去。
2.较低的生产成本，由于模具冷却水道不受腐蚀的影响（不象普通模具钢），热传导特性、冷却效率在模具生命期中均保持稳定，确保了模具恒久不变的成形时间。STAVAX ESR(S-136)被推荐用于所有的模具，由于其特殊的性质，更适合特殊环境的需求。我们来看下不同牌号红铜特性，如下1、C1100：具有较高之热电传导性、加工性、延展性、耐蚀性和耐候性。
3. 耐腐蚀、锈蚀对使用有腐蚀性的PVC、醋酸盐类等注模原料或必须在潮湿的环境下工作及存放的模具。
4.性在使用磨耗较大的注模材料（包括热固性射出成型模）或要求模具有较长的工作时间，如电子零件、舍弃式的餐刀具、器皿等。
5.高光滑度的表面生产光学产品，如照相机、太阳眼镜、化学仪器及塑料制品等。