电极红铜分类
紫铜类（纯铜）：T2.C1100.C11000.无氧铜TU1.C1020.C10200加磷脱氧铜TP2.C1220.C12200.
黄铜类，铜合金
H96.C2100.C21000.H90.C2200.C22000.H85.C2300.C23000.H80.C2400.C24000.H68A.C2680. C26200.H65.C2700.C26800.H62
五金模具钢现货供应
电极红铜分类
紫铜类（纯铜）：T2.C1100.C11000.无氧铜TU1.C1020.C10200加磷脱氧铜TP2.C1220.C12200.
黄铜类，铜合金
H96.C2100.C21000.H90.C2200.C22000.H85.C2300.C23000.H80.C2400.C24000.H68A.C2680. C26200.H65.C2700.C26800.H62.C2720.C27400.
铅黄铜 HPb59-1.C3710.C37800.HPb59-2.C3771.C35300. HPb60-2.C3604.C36000.HPb63-3.C3560.C34500.HPb63-0.1.C34900.
铝黄铜HAi77-2.C6870.C68700. HAi60-1-1.C6782.C67000.HAi59-3-2.C67800.HAi66-6-3-2.C6872.
锡黄铜HSn62-1.HSn70-1AB.锰黄铜HMn58-2.C67400.HMn57-3-1.铁黄铜HFe59-1-1.C6782.C67820.硅黄铜HSi80-3.C69400.
青铜类：
锡青铜QSn4-3,QSn6.5-0.1.QSn7-0.2.C5212.C52100.QSn6.5-0.4.
铝青铜QAi9-2.C61000.QAi9-4.QAi10-3-1.5. C6161.C61900.QAi10--4-4.C6301.C63000.C63200.
硅青铜QSi3-1.C65500.C65800.QSi1-3.C64700.QSi1.8. 锰青铜QMn5.锆青铜QZr0.2-0.4.铬青铜QCr0.5.C18100.C18200.C18400.QCr1-2.
铬锆铜QCr1-0.15.C18150. 镉青铜QCd1.0.铍青铜QBe1.8.QBe2.0.白铜类：B19.B25.铁白铜BFe10-1--1.B111.C70600.BFe30--1-1.B111. C71500.
锌白铜BZn15-20.等。
电极红铜
红铜特点及用途：
红铜就是铜单质.因其颜色为紫红色而得名,又名紫铜 纯铜 赤铜 电极铜 。S136模具钢那么有什么好的方法预防呢，下面我们来解析下出现这种情况的原因及处理对策。红铜是工业纯铜,高纯度，具有良好的导电性，导热性，高延伸性，耐腐蚀性，耐大气腐蚀性,耐候性。还可加入其他元素,以改善材质和性能,如加入0.3%-2%的碲构成高铜合金,加入0.4%-1.2%的铬构成铬铜合金等。红铜是用途广泛的电极铜，被广泛用于制造电线、电缆、电刷、电火花，制作导电、导热器材，化学工业等行业。
化学成份力学性能参考：
含铜99.95%， 含氧率（0.02-0.05%) 导电率 (IACS)101% 硬度(HV) ：约85.2-110 密度(比重):约8.9
出货地点：
品名：红铜 紫铜 赤铜 电极铜 纯铜 电解铜 电蚀铜 C1100铜 二号铜 T2铜 导电铜 导热铜 耐腐蚀铜 工业铜 产地：日本/台湾/ 铜含量：99.95（%）