电极红铜分类
紫铜类（纯铜）：T2.C1100.C11000.无氧铜TU1.C1020.C10200加磷脱氧铜TP2.C1220.C12200.
黄铜类，铜合金
H96.C2100.C21000.H90.C2200.C22000.H85.C2300.C23000.H80.C2400.C24000.H68A.C2680. C26200.H65.C2700.C26800.H62
塑胶制模用品厂家
电极红铜分类
紫铜类（纯铜）：T2.C1100.C11000.无氧铜TU1.C1020.C10200加磷脱氧铜TP2.C1220.C12200.
黄铜类，铜合金
H96.C2100.C21000.H90.C2200.C22000.H85.C2300.C23000.H80.C2400.C24000.H68A.C2680. C26200.H65.C2700.C26800.H62.C2720.C27400.
铅黄铜 HPb59-1.C3710.C37800.HPb59-2.C3771.C35300. HPb60-2.C3604.C36000.HPb63-3.C3560.C34500.HPb63-0.1.C34900.
铝黄铜HAi77-2.C6870.C68700. HAi60-1-1.C6782.C67000.HAi59-3-2.C67800.HAi66-6-3-2.C6872.
锡黄铜HSn62-1.HSn70-1AB.锰黄铜HMn58-2.C67400.HMn57-3-1.铁黄铜HFe59-1-1.C6782.C67820.硅黄铜HSi80-3.C69400.
青铜类：
锡青铜QSn4-3,QSn6.5-0.1.QSn7-0.2.C5212.C52100.QSn6.5-0.4.
铝青铜QAi9-2.C61000.QAi9-4.QAi10-3-1.5. C6161.C61900.QAi10--4-4.C6301.C63000.C63200.
硅青铜QSi3-1.C65500.C65800.QSi1-3.C64700.QSi1.8. 锰青铜QMn5.锆青铜QZr0.2-0.4.铬青铜QCr0.5.C18100.C18200.C18400.QCr1-2.
铬锆铜QCr1-0.15.C18150. 镉青铜QCd1.0.铍青铜QBe1.8.QBe2.0.白铜类：B19.B25.铁白铜BFe10-1--1.B111.C70600.BFe30--1-1.B111. C71500.
锌白铜BZn15-20.等。
s136优点
1. 较低的维修费用模具经过长期使用后，模穴表面仍然维持原先的光滑状态。模具在潮湿的环境下操作或存放时、不需要特别的保护。
一看全懂了！机械、模具加工常用金属材料及其特性！
2.较低的生产成本，由于模具冷却水道不受腐蚀的影响（不象普通模具钢），热传导特性、冷却效率在模具生命期中均保持稳定，确保了模具恒久不变的成形时间。STAVAX ESR(S-136)被推荐用于所有的模具，由于其特殊的性质，更适合特殊环境的需求。锰铜﹑康铜﹑考铜是含锰量不同的锰白铜﹐是制造精密电工仪器﹑变阻器﹑精密电阻﹑应变片﹑热电偶等用的材料。
2.淬火温度过高
这是由工艺设置温度不当或控温系统误差造成，应当修正工艺温度，检修校核控温系统。
3.过回火
这是由回火温度设置过高、控温系统故障误差或炉温过高时入炉造成，应当修正工艺温度，检修校核控温系统，不高于设置炉温装入。
4.冷却不当
原因是预冷时间过长，冷却介质选择不当，淬火介质温度渐高而冷却性能下降，搅拌不良或出槽温度过高等。
解决措施：出炉、入槽等要快；掌握淬火介质冷却特性；油温60-80℃，水温30℃以下，当淬火量大而使冷却介质升温时，应添加冷却淬火介质或改用其它冷却槽冷却；加强冷却剂的搅拌；在Ms+50℃时取出。